        化學交聯聚乙烯絕緣料 XEJ-10 XEJ-35
        Chemical Cross-Linkable PE Insulation Compound...
        型號:0

        參考價:¥

        說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。

        Product description產品描述
        Chemical cross-linkable PE insulation compound for power cables which regards advanced LDPE resin as the main raw material, adds antioxidant, cross-linking agent and other accessory ingredients, is manufactured by advanced closed extruding equipment. It has excellent extrusion property and physical property, its impurity content is controlled within limits. This product is mainly used as the insulation of medium-low voltage cross-linking cables. Long-term working temperature is 90℃.
        電力電纜用可化學交聯聚乙烯絕緣料是以優質低密度聚乙烯樹脂為主要原材料,加入抗氧劑、交聯劑等助劑,采用先進的封閉式混煉裝置加工而成,它兼有良好的擠出性能和物理性能,雜質含量符合要求,專用于生產中、低壓交聯電線電纜,長期工作溫度為90℃。
         
         
        Processing Indicator 加工工藝
        Recommend to process with the PE extruder
        建議使用聚乙烯專用擠出機進行加工。


        Model
        牌號
        Machine Barrel Temperature
        機筒溫度
        Molding Temprature
        機頭溫度
        XEJ-10/ XEJ-35 100-115℃ 110-115℃
         
         
         
        Physical and Electrical Properties 物理和電氣性能

        Item

        試驗項目

        Unit
        單位

        Standard Data

        標準值

        XEJ-10 XEJ-35
        Density
        密度
        g/cm3 0.922±0.003 0.922±0.003
        Tensile Strength
        拉伸強度
        MPa ≥13.5 ≥13.5
        Elongation at Break
        斷裂伸長率
        % ≥350 ≥350
        Brittle Temperature with Low Temperature
        低溫脆化溫度
        -76 -76
        20℃Volume Resistivity
        20℃體積電阻率
        Ω·m ≥1.0×1014 ≥1.0×1014
        20℃Dielectric Strength,50Hz
        20℃介電強度, 50Hz
        MV/m ≥25.0 ≥25.0
        20℃Dielectric Constant,50Hz
        20℃介電常數, 50Hz
        --- ≤2.35 ≤2.35
        20℃Dielectric Dissipation Factor,50Hz
        20℃介質損耗因數, 50Hz
        --- ≤0.001 ≤0.0005
        Impurity Content(Per 1.0Kg)
        雜質含量(每1.0Kg)
        0.175-0.250 mm
        ≥0.250 mm
         
         
        個(No.)
        個(No.)
        ---  
         
        ≤5
        0
        Air Aging Condition
        熱空氣老化條件
        135℃×168h
        Tensile Strength Variation After Aging
        拉伸強度變化率
        % ≤±20 ≤±20
        Elongation Variation After Aging
        斷裂伸長變化率
        % ≤±20 ≤±20
        Hot Set Test Condition
        熱延伸試驗條件
        200℃×0.2MPa×15min
        Hot Elongation
        負荷下伸長率
        % ≤80 ≤80